Hybrid Ion Conductors Membrane for CO2 Separation

Abstract

CO2 is emitted in a very large amount per year by the different fossil fuel industries for the generation of energy which is the major origin of GHG in the climate. CO2 emission is a major worldwide problem of today. Different works have been done for the reduction of CO2 emission gas and numerous types of works are under process. In our project the major focus is to separate the CO2 by hybrid ion conductors membrane of solid oxide fuel cell. For this purpose, GDC/Li2CO3-Na2CO3 (LN-GDC) nanocomposite electrolyte material was synthesized with molar ratio 1:3 by co precipitation method. The sample was dried in oven and filtered by suction pump followed by sintering at temperature 700oC in a digital furnace. The prepared sample LN-GDC was further characterized by different techniques; XRD, SEM, FTIR including conductivity measurements by four probes DC method. The XRD and SEM results confirm that the synthesized material lies in nano scale, homogeneous and dense in nature. However, the major study was focused to analyze the CO2 separation from this membrane so the sample was further reformed in polymer membrane and chloroform was used as a solvent for the preparation of dense hybrid membrane. This modified prepared hybrid membrane is used for the separation of CO2 gas